ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M Introduction
ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M Material, A1011 HSLAS-F Grade 80 steel,A1011 HSLAS-F Grade 80 steel hardness, A1011 HSLAS-F Grade 80 plate weight, A1011 HSLAS-F Grade 80 plate size, A1011 HSLAS-F Grade 80 plate thickness, ASTM A1011/A1011M Germany DIN equivalent, ASTM A1011/A1011M steel manufacturer in China, ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M steel mechanical properties, ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M steel in Malaysia, ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M steel in Dubai
Application: Standard Specification for Steel Sheet and Strip, Hot-Rolled, Carbon, Structural, High-Strength Low-Alloy, High-Strength Low-Alloy with Improved Formability.
Heat treated: 1636°C - 1172°C.
ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M Chemical Element
What is the chemical composition of ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M? For ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M element content, please contact us.
| Element | Min | Max | Similar |
|---|---|---|---|
| V | 0.0050 | - | - |
| Ti | 0.0050 | - | - |
| S | - | 0.0250 | - |
| P | - | 0.0200 | - |
| Ni | - | 0.2000 | - |
| Nb | 0.0050 | - | - |
| N | - | - | - |
| Mo | - | 0.1600 | - |
| Mn | - | 1.6500 | - |
| Cu | - | 0.2000 | - |
| Cr | - | 0.1500 | - |
| C | - | 0.1500 | - |
ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M Mechanical Properties
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 663 (≥) | 632 (≥) | 22 | 24 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 244 |
ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M Physical Properties
Physical properties of ASTM A1011 HSLAS-F Grade 80 ASTM A1011/A1011M are mainly indicated by modulus of electrical resistance value, thermal conductivity, specific thermal capacity, coefficient of thermal expansion, elasticity, poisson's ratio, density, etc.
| Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson's coefficient, ν |
|---|---|---|---|---|---|---|---|
| 13 | - | - | 0.32 | - | |||
| 812 | 441 | - | 32.3 | 144 | - | ||
| 437 | - | 14 | 32.2 | 123 | 311 |