Chemical Composition Of ASTM A572 Gr.60 Plates
| Grade | C % | Si % | Mn % | P % | S % | V % | Ni % | Co % |
| A572 Gr.60 | 0.260 | 0.400 | 1.350 | 0.040 | 0.050 | 0.060 | 0.015 | 0.050 |
Mechanical Properties Of ASTM A572 Gr.60 Plates
| Grade | Thickness(mm) | Min Yield (Mpa) | Tensile(MPa) | Elongation(%) |
| A572 Gr.60 | 8mm-50mm | 415Mpa | 520Mpa | 20% |
| 50mm-200mm | 415Mpa | 520Mpa | 24% | |
| The min impact energy is longitudinal energy | ||||
In addition, this steel plate offers good weldability and resistance to lamellar tearing. During welding, either manual or automatic welding can be selected, and appropriate welding processes should be applied to ensure the quality of the weld. Resistance to lamellar tearing refers to the ability of the steel plate to maintain good plasticity and toughness after welding and other heat treatments.
In terms of thickness, SA572 Grade 60 steel plate can be processed into various sizes, including 8–200 mm × 2000–3000 mm × 8000–12000 mm.
In summary, SA572 Grade 60 is a high-strength low-alloy steel plate with good weldability and resistance to lamellar tearing, widely used in various mechanical parts and structural components.