Characteristics of S690Q-brand steel
S690Q is a hot-rolled hardened structural steel that has undergone subsequent tempering treatment and conforms to the EN 10025-6, DSTU EN 10025-6 standard.
- Standard: Hot-rolled product made from structural steel. EN 10025-6: Technical delivery conditions for high-tensile structural steel post-tempering and quenching.
- Classification: High-grade structural steel.
- Product:Fine-grain steel post-quenching and tempering.
Chemical Composition and Mechanical Property
|
S690Q Chemical Composition |
||||||||
|
Grade |
The Element Max (%) |
|||||||
|
C |
Si |
Mn |
P |
S |
N |
B |
Cr |
|
|
S690 Q |
0.20 |
0.80 |
1.70 |
0.020-0.025 |
0.010-0.015 |
0.015 |
0.005 |
1.50 |
|
Cu |
Mo |
Nb |
Ni |
Ti |
V |
Zr |
|
|
|
0.50 |
0.70 |
0.06 |
2.0 |
0.05 |
0.12 |
0.15 |
|
|
|
Grade |
S690Q Mechanical Property |
|||||
|
Thickness |
Yield |
Tensile |
Elongation |
Min Impact Energy
|
||
|
S690 Q |
mm |
Min Mpa |
Mpa |
Min % |
-20 |
30J |
|
3 |
690 |
770-940 |
14 |
-20 |
30J |
|
|
50 |
650 |
760-930 |
14 |
-20 |
30J |
|
|
100 |
630 |
710-900 |
14 |
-20 |
30J |
|
EN 10025-2 S690Q Sheet and Plates EQUIVALENT GRADE
| Standard | ASTM | DIN, WNr | JIS | AFNOR | ISO 4952 |
| EN 10025-2:2004 | A709-100 | TStE690V DILLIMAX 690 NAXTRA 70 | JFE HITEN 780LE | E690T E690TFP S690T | E690 |
Technical Requirements & Additional Services for S690Q steel plate
♦ Low temperature impacting test
♦ Quenching and Tempering heat treatment
♦ Ultrasonic test under EN 10160,ASTM A435,A577,A578
♦ Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
♦ Shot blasting and Painting,Cutting and welding as per end user's demands
S690Q steel plate production process
1. Raw materials (scrap steel, pig iron and molten iron)
2. Electric furnace (100-ton electric arc furnace smelting), converter
3. LF furnace molten steel refining treatment
4. Vacuum treatment of molten steel in VD or VOD furnace
5. Die casting (a variety of key-type die casting lines) or continuous casting (large slab continuous casting machine); (one ingot remelting 50 tons slab type electroslag furnace)
6. Heating (continuous furnace and soaking furnace)
7. Steel plate rolling (4100 and 4200mm mills)
8. Heat treatment of steel plate (normalizing and tempering)
9. Steel plate cutting inspection
10. Storage
If you want to learn more about GNEE's products, you can send an email to alloy@gneesteelgroup.com. We are more than happy to assist you.
FAQ
What is the difference between S690Q and S690QL?
S690Q: Minimum impact toughness tested at -20°C (30J average). → Typical Use: Cranes in temperate climates, quarry equipment. S690QL: Certified for -40°C and below (≥40J impact toughness). → Critical Use: Arctic pipelines, offshore platforms, mining vehicles in Siberia.
What grade is S690QL material?
S690QL is a high strength quenched and tempered steel grade that complies to steel specification EN 10025. The designation S690QL refers to a minimum yield strength of 690 MPa.
What is S690 grade steel?
S690 high yield & fine grain steel plate is a high strength, quenched and tempered fine-grain structural steel. Structural steel S690 is used in structures that must withstand very heavy loads. This grade is meant for structures where weight savings is important.
What is the equivalent of S690 steel?
Approximate equivalents
ASTM A514, EN 10149-2 Grade S700MC, AS/NZS 3579 Grade 700, AM 700, Bisalloy 80.
What is the price of S690QL material?
S690QL High Strength Steel Plates, Thickness: 5mm to 150mm at ₹ 135/kilogram in Mumbai.
What is the hardness of S690 QL steel?
S690QL steel stockholders and suppliers. S690QL is a quenched and tempered high strength steel supplied in full plates or cut pieces with delivery to the whole of the UK. With its high yield of minimum 690MPa it offers better strength than standard carbon steel grades.
What is the effective use of high strength S690 steel in construction?
The high strength S690 steels have an excellent strength-to-self-weight ratio, and they are highly efficient to be used in heavily loaded structures. Typical applications include piles and columns in buildings and supporting members in bridges.
What is the difference between S890QL and S690QL?
S690QL, S890QL, and S960QL are all water quenched and tempered steels that comply with the EN10025:6:2004 specification. These ultra high strength steels have a minimum yield strength of 690 MPa, 890 MPa, and 960 Mpa respectively, making them ideal for use in the haulage sector.
What is the difference between S700MC and S690ql?
The S700MC Steel is basically a structural steel plate developed especially for applications requiring high yield strength. They are used for several load bearing applications. The S690ql is a low alloy structural steel which is high in strength and comes with good weldability.
What is the yield strength of s690 steel?
690 MPa.
Yield strength of 690 MPa. Used in structures bearing extremely heavy loads, such as bridges, offshore drilling rigs and buildings, as well as in heavy construction equipment and cranes.