ASTM A387 Gr 22 CL 1 is a chromium molybdenum alloy steel plate intended primarily for welded boiler and pressure vessels designed of elevated temperature service. The Cr content 2.25 % and the Mo content 1.00 %.
STEEL DIMENSION:
Thickness: 6MM to 300MM,
Width: 1500mm to 4050mm,
Length: 3000mm to 15000mm
Equivalents for ASTM A387 Grade 22 Alloy Steel Plates
| BS | EN | ASTM/ASME | DIN |
| 622-515B | 10 CRMO910 | A387-22-1 | 10 CRMO910 |
Specifications for ASTM A387 Grade 22 Alloy Steel Plates
Chromium & Molybdenum content (according to the ASME specification)
| Designation | Nominal Chromium Content (%) |
Nominal Molybdenum Content (%) |
| A387 Grade 22 | 2.25% | 1.00% |
Tensile Requirements for ASTM A387 Grade 22 Alloy Steel Plates Class 1 Plates
| Designation: | Requirement: | Grade 22 |
| A387 Grade 22 | Tensile strength, ksi [MPA] | 75 to 100 [515 to 690] |
| Yield strength, min, ksi [MPa]/(0.2% offset) | 45 [310] | |
| Elongation in 8 in. [200mm], min % | ... | |
| Elongation in 2 in. [50mm], min, % | 18 | |
| Reduction of area, min % | 45 (measured on round specimen) 40 (measured on flat specimen) |
Chemical Requirements for ASTM A387 Grade 22 Alloy Steel Plates
| Element | Chemical Composition (%) | |
| A387 Grade 22 | ||
| Carbon: | Heat Analysis: | 0.05 - 0.15 |
| Product Analysis: | 0.04 - 0.15 | |
| Manganese: | Heat Analysis: | 0.30 - 0.60 |
| Product Analysis: | 0.25 - 0.66 | |
| Phosphorus: | Heat Analysis: | 0.035 |
| Product Analysis: | 0.035 | |
| Sulphur (max): | Heat Analysis: | 0.035 |
| Product Analysis: | 0.035 | |
| Silicon: | Heat Analysis: | 0.50 max |
| Product Analysis: | 0.50 max | |
| Chromium: | Heat Analysis: | 2.00 - 2.50 |
| Product Analysis: | 1.88 - 2.62 | |
| Molybdenum: | Heat Analysis: | 0.90 - 1.10 |
| Product Analysis: | 0.85 - 1.15 |