NM450 wear-resistant steel plate is a kind of domestic wear-resistant steel plate. After hot rolling, it is heat treated by direct quenching and tempering and reheating quenching and tempering processes. It has high mechanical strength, which is 3 to 5 times that of ordinary low-alloy steel plates. The surface hardness can be significantly improved, generally reaching 360~450HB.
Chemical Composition Of NM 450 Plates:
| NM450 Chemical Compositiom | |||||||||||
| Plate | C | Si | Mn | P | S | Cr | Ni | Mo | B | CEV | CET |
| thickness mm | max % | max % | max % | max % | max % | max % | max % | max % | max % | typv | typv |
| 3-(8) | 0.19 | 0.7 | 1.6 | 0.025 | 0.01 | 0.25 | 0.25 | 0.25 | 0.004 | 0.41 | 0.30 |
| 8-20 | 0.21 | 0.7 | 1.6 | 0.025 | 0.01 | 0.50 | 0.25 | 0.25 | 0.004 | 0.47 | 0.34 |
| (20)-40 | 0.23 | 0.7 | 1.6 | 0.025 | 0.01 | 1.00 | 0.25 | 0.25 | 0.004 | 0.57 | 0.37 |
| (40)-50 | 0.23 | 0.7 | 1.6 | 0.025 | 0.01 | 1.40 | 0.25 | 0.60 | 0.004 | 0.59 | 0.36 |
| (50)-80 | 0.26 | 0.7 | 1.6 | 0.025 | 0.01 | 1.40 | 1.00 | 0.60 | 0.004 | 0.72 | 0.41 |
Mechanical Properties for NM 450 High Tensile Plate:
| Mechanical properties of NM 450 | |||||
| Thickness/mm | ReL /MPa | Rm /MPa | A/% | Hardness/ HBW10/3000 | Impact -20℃ /J |
| 8 | 1250 | 1460 | 16 | 445 | 40 |
| 12 | 1290 | 1470 | 17 | 462 | 43 |
| 20 | 1370 | 1450 | 17 | 473 | 42 |
| 25 | 1230 | 1480 | 16.5 | 465 | 43 |
GNEE Group NM450 wear-resistant steel plate inspection pictures: