ASTM A387 Gr 12 CL 1 is a chromium molybdenum alloy steel plate intended primarily for welded boiler and pressure vessels designed of elevated temperature service. The Cr content 1.00% and the Mo content 0.5%. Engineered for use in elevated temperature service, is a chrome molybdenum carbon alloy steel for use in weldable pressure vessels and industrial boilers.
The material benefits from added chromium which provides excellent corrosion and oxidation resistance making it ideal for sour service applications in the oil and gas industry.
Supplementary Technology: HIC Test | NACE MR0175 | Z15 | Z25 | Z35 | S1 | S2 | S3 | S4
S5 | S6 | S7 | S8 | S9| S11 | S12 | S14 | S17
STEEL DIMENSION:
Thickness: 6MM to 300MM,
Width: 1500mm to 4050mm,
Length: 3000mm to 15000mm
Equivalents
| BS | EN | ASTM/ASME | DIN |
| 620 B | 13 CRMO 45 | A387-12-1 | 13 CRMO 44 |
Specifications for ASTM A387 Grade 12 Alloy Steel Plates
Chromium & Molybdenum content (according to the ASME specification)
| Designation | Nominal Chromium Content (%) |
Nominal Molybdenum Content (%) |
| A387 Grade 12 | 1.00% | 0.50% |
Tensile Requirements for ASTM A387 Grade 12 Alloy Steel Plates Class 1 Plates
| Designation: | Requirement: | Grade 12 |
| A387 Grade 12 | Tensile strength, ksi [MPA] | 65 to 85 [450 to 585] |
| Yield strength, min, ksi [MPa]/(0.2% offset) | 40 [275] | |
| Elongation in 8 in. [200mm], min % | 19 | |
| Elongation in 2 in. [50mm], min, % | 22 | |
| Reduction of area, min % | ––– |
Chemical Requirements for ASTM A387 Grade 12 Alloy Steel Plates
| Element | Chemical Composition (%) | |
| ASTM A387 Grade 12 | ||
| Carbon: | Heat Analysis: | 0.05 - 0.17 |
| Product Analysis: | 0.04 - 0.17 | |
| Manganese: | Heat Analysis: | 0.40 - 0.65 |
| Product Analysis: | 0.35 - 0.73 | |
| Phosphorus: | Heat Analysis: | 0.035 |
| Product Analysis: | 0.035 | |
| Sulphur (max): | Heat Analysis: | 0.035 |
| Product Analysis: | 0.035 | |
| Silicon: | Heat Analysis: | 0.15 - 0.40 |
| Product Analysis: | 0.13 - 0.45 | |
| Chromium: | Heat Analysis: | 0.80 - 1.15 |
| Product Analysis: | 0.74 - 1.21 | |
| Molybdenum: | Heat Analysis: | 0.45 - 0.60 |
| Product Analysis: | 0.40 - 0.65 |