A537CL1+410 Clad plate is a highly efficient and green material, which features qualities of stainless steel: Corrosion resistance, oxidation resistance, wear resistance, bonding proof and acid-base resistance; With 50years of service life; Low carbon steel price; And ensures its good strength, toughness, bending and stretching, impact resistance. Our products are widely applied in fields such as petroleum, chemistry, electricity, paper making, alkali making, irrigation works, automotives, salt, medicine, food and public facilities.
Are widely applied to Petroleum, Chemical Factory and the Boilers domains. They are also made the Reactor, Heat Exchange, Separator, Spherical Tank, the Tank of oil gas, reactor pressure shell, High-pressure water pipe, Turbine shell and other equipments.
A537CL1+410 Clad steel plate Chemical Composition and Mechanical Property
|
ASTM A537 Class 1 Chemical Composition |
|||||||
|
Grade |
The Element Max (%) |
||||||
|
C |
Si |
Mn |
P |
S |
Al |
N |
|
|
A537 Class 1 |
0.24 |
0.13–0.55 |
0.64-1.46 |
0,035 |
0,035 |
|
|
|
Nb |
V |
Ti |
Cu |
Cr |
Ni |
Mo |
|
|
|
|
|
0.38 |
0.29 |
0.28 |
0.09
|
|
|
Grade |
|
ASTM A537 Class 1 Mechanical Property |
||
|
Thickness |
Yield |
Tensile |
Elongation |
|
|
A537 Class 1 |
mm |
Min Mpa |
Mpa |
Min % |
|
6-65 |
345 |
485-620 |
22% |
|
|
65-100 |
310 |
450-585 |
|
|
|
100-150 |
|
|
18% |
|
| Grade |
C
|
Mn |
P
|
S
|
Si |
Cr |
Ni | Mo | Ni |
Cooper
|
| 410(S41000) | 0.08-0.15 | 1.00 | 0.040 | 0.030 | 1.00 | 11.5-13.5 | 0.75 | - | - | - |
| Grade |
Yield strength (N/mm2), min |
Tensile strength (N/mm2), min |
Elongation in 2 in. (50mm), %, min |
|
Cold bend | ||||||
|
Austenitic (Chromium-Nickel) (Chromium-Manganese-Nickel) |
|||||||||||
| 410(S41000) |
|
|
20 |
|
180 | ||||||
Performances of Stainless Steel Clad Plate
The carbon steel and stainless steel usually form a metallurgical bond during heating and rolling by hot rolling or explosion bonding or the combination of both and the standard method of producing clad steel is hot roll cladding method.
Hot roll bonding is a commonly used process in our stainless steel clad plate factory. During this process, clean sheets of carbon steel and stainless steel are placed on each other, (single-sided cladding), or sandwiched between two stainless steel sheets (double-sided cladding). The composite sheets are hot rolled together.
The stainless steel cladding process results in a bond between the two metals. Another manufacturing method is explosive bonding. The metals bond during the explosion due to the plastic deformation of the strong collision. Explosive bonding after the hot rolling process can improve the bond between carbon steel and stainless steel.
Duplex Stainless Steel Cladding
Duplex stainless steel has higher strength, higher corrosion resistance and lower price. The thickness of the sheet can be reduced to maintain strength, so it can be used to make structural units such as pressure vessels, chemical storage tanks, bridges, hot water tanks and processing plants. In recent years, storage equipment and industrial storage tanks in the paper industry, sugar industry, have adopted stainless steel clad plates.
A537CL1+410 Clad steel plate Other Name
A537CL1+410 Clad steel plate, A537CL1 steel plate, 410 steel plate
For sanitary pressure vessels in pharmaceutical/food industries (e.g., sterile drug storage tanks, dairy processing equipment), we provide Q345B+304L Clad steel or Q235B+304 Clad steel that meets TSG 21 and food-grade standards. If you need to know surface roughness requirements, weldability with sanitary fittings, or calculate processing costs for customized inner cavities, send an inquiry for professional consultation and certification documents.