A516Gr70(NACE)+410 Clad steel plate Chemical Composition and Mechanical Property
|
Grade |
Chemical Composition(%) |
||||||
|
C |
Mn |
Si |
P max |
S max |
|||
|
|
0.27-0.31 |
0.79-1.3 |
0.13-0.45 |
0.035 |
0.035 |
||
|
Grade |
Mechanical Property |
|
|||||
|
Tensile Strength(MPa) |
Yield Strength(MPa) min |
% Elongation in 2 in.(50mm) min |
Impacting Test Temperature(°C) |
|
|||
|
|
485-620 |
260 |
17 |
-20,40,-60 |
|
||
| Grade |
C
|
Mn |
P
|
S
|
Si |
Cr |
Ni | Mo | Ni |
Cooper
|
| 410(S41000) | 0.08-0.15 | 1.00 | 0.040 | 0.030 | 1.00 | 11.5-13.5 | 0.75 | - | - | - |
| Grade |
Yield strength (N/mm2), min |
Tensile strength (N/mm2), min |
Elongation in 2 in. (50mm), %, min |
|
Cold bend | ||||||
|
Austenitic (Chromium-Nickel) (Chromium-Manganese-Nickel) |
|||||||||||
| 410(S41000) |
|
|
20 |
|
180 | ||||||
A516Gr70(NACE)+410 Clad plate Application
A516Gr70(NACE)+410 Clad steel plates are used in Construction of Bridges, Highway Construction and Other Engineering construction.
A516Gr70(NACE)+410 Composite steel plate Other Name
A516Gr70(NACE)+410 Clad steel plate, A516Gr70(NACE) steel plate, 410 steel plate
Additional Condition
UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.
Collaborative Project
| Specifications | Quantit (MT) |
Specific Applications | |
| Q345R+316L | 12+2 | 1800MT | Coal-to-Ethylene Glycol Project |
| Q345R+S30408 | 8+2/10+2 | 700MT | Ethylene Glycol Storage Tank |
| Q345R+S31603 | 8+2/10+2 | 600MT | Paraffin wax |
| Q370QE+316L | 16+3 | 1600MT | Clad Plate for bridge decks |
| Q370QE+316L | 16+3 | 1800MT | Clad Plate for bridge decks |
| Q345R+316L | 28+3 | 400MT | Pressure Vessel |
| Q235B+1Cr13 | 8+2 | 800MT | Building mold table |
| Q235B+1Cr13 | 8+2 | 800MT | Building mold table |
| Q235A+1Cr13 | 8+2 | 620MT | Building mold table |
| Q235A+1Cr13 | 8+2 | 300MT | Building mold table |
| Q235A+1Cr13 | 8+2 | 570MT | Building mold table |
| Q235A+1Cr13 | 8+2 | 600MT | Building mold table |
| Q345B+304 | 6+2/30+2 | 980MT | Pulp tower |
| Q235B+304 | 6+2/22+2 | 1000MT | Pulp tower |
| Q345R+304 | 6+2/16+2 | 600MT | Pulp tower |
| Q345R+304 | 6+2/20+2 | 1400MT | Pulp tower |
| Q345R+304 | 16+2/8+2 | 780MT | Pulp tower |
| Q235B+304 | 20+2 | 800MT | Pulp tower |
Suitable for chemical anti-corrosion equipment (e.g., hydrochloric acid storage tanks, alkaline solution reactors), using clad steel plates like A516Gr70+316L Clad steel or A516Gr70+904L Clad steel. If you need to confirm corrosion resistance data in harsh media, bonding strength between base and cladding layers, or get a customized quotation for sizes (thickness 6–100mm), send an inquiry to obtain detailed material specifications and tailored solutions.
Email: alloy@gneesteelgroup.com
Whatsapp (WeChat): +86 15824687445
In addition to Clad steel plate, we also offer a variety of steel plate types, as shown in the table below, that are suited for different scenarios – including high-strength low-alloy plates for petrochemical high-pressure conditions, wear-resistant plates for mining heavy-duty wear, weather-resistant plates for outdoor harsh environments, and marine plates that meet shipbuilding standards. If you are looking for steel plates for specific applications, feel free to contact us anytime.
Hot Tags: a516gr70(nace)+410 clad steel plate, China a516gr70(nace)+410 clad steel plate manufacturers, suppliers, factory