What is the temperature range for P355GH?
EN 10028-2 Grade P355GH Pressure Vessel Steel Plate Suitable Up to 400 ºC Temperature.
P355GH VS S355J2
P355GH Chemical composition
|
P355GH Chemical Composition |
|||||||
|
Grade |
The Element Max (%) |
||||||
|
C |
Si |
Mn |
P |
S |
Al(min) |
N |
|
|
P355GH |
0.10-0.22 |
0.60 |
1.10-1.70 |
0.025 |
0.015 |
0.020 |
0.012 |
|
Cr |
Cu |
Mo |
Nb |
Ni |
Ti |
V |
|
|
0.30 |
0.30 |
0.08 |
0.040 |
0.30 |
0.03 |
0.02 |
|
S355J2 Chemical composition
|
C |
Si |
Mn |
Ni |
P |
S |
Cr |
Mo |
|
max 0.24 |
0.60 |
1.70 |
|
Max 0.035 |
Max 0.035 |
|
|
|
V |
Nb |
Ti |
N |
Cu |
|
|
|
|
|
|
|
|
0.60 |
|
|
|
P355GH Mechanical Property
|
Grade |
|
P355GH Mechanical Property |
|||||
|
Thickness |
Yield |
Tensilmie |
Elongation |
Impact Energy(KV J) min |
|||
|
P355GH |
mm |
Min Mpa |
Mpa |
Min % |
-20° |
0° |
+20° |
|
≤ 16 |
355 |
510-650 |
20 |
27 |
34 |
40 |
|
|
16> to ≤40 |
345 |
510-650 |
20 |
27 |
34 |
40 |
|
|
40> to ≤60 |
335 |
510-650 |
20 |
27 |
34 |
40 |
|
|
60> to ≤100 |
315 |
490-630 |
20 |
27 |
34 |
40 |
|
|
100> to ≤150 |
295 |
480-630 |
20 |
27 |
34 |
40 |
|
|
150> to ≤250 |
280 |
470-630 |
20 |
27 |
34 |
40 |
|
S355J2 Mechanical Property
|
|
-150 |
150-250 |
250-400 |
|
|||||||||||
|
Minimum energy nominal thicknessTemperature(-20) |
27 |
27 |
27 |
|
|||||||||||
|
Nominal thickness (mm) |
to 16 |
16 - 40 |
40 - 63 |
63 - 80 |
80 - 100 |
100 - 150 |
150 - 200 |
200-250 |
250-400 |
||||||
|
ReH - Minimum yield strength (MPa) |
355 |
345 |
335 |
325 |
315 |
295 |
285 |
275 |
265 |
||||||
|
Nominal thickness (mm) |
-3 |
3-100 |
100-150 |
150-250 |
250-400 |
||||||||||
|
Rm -Tensile strength (MPa) |
510-680 |
470-630 |
450-600 |
450-600 |
450-600 |
||||||||||
|
Nominal thickness (mm) |
3-40 |
40-63 |
63-100 |
100-150 |
150-250 |
250-400 |
|
A - Minimum elongation Lo = 5,65 √ So (%) |
22 |
21 |
20 |
18 |
17 |
17 |